I-Calcium Aluminate Cement, High Aluminate Cement A600, A700.G9, CA-70, CA-80

Incazelo emfushane

I-porosity ephansi, ukuzinza okuphezulu kwamakhemikhali, ukusebenza okuphezulu kwezinga lokushisa, ukumelana nokugqoka okuphezulu

XHUMANA MANJE

Izici

I-porosity ephansi, ukuzinza okuphezulu kwamakhemikhali, ukusebenza okuphezulu kwezinga lokushisa, ukumelana nokugqoka okuphezulu

Imininingwane imininingwane

Umkhiqizo uvame ukusetshenziswa njengezinto ezahlukahlukene zokushisela i-metallurgy, i-petrochemical, i-petroleum, imishini, izinto zokwakha nezinye izimboni.

I-Alumina Cement ephezulu CA-50

Izinto			Iyunithi	A600	A700	G9
Ukwakheka kwamakhemikhali	Al₂O₃		%	50-60	50-60	53.5 ubuningi
	I-CaO		%	33 imiz	33.00 min	33.00 min
	SiO₂		%	8.00 ubuningi	8.00 ubuningi	5.50 ubuningi
	Fe₂O₃		%	2.50 ubuningi	2.50 ubuningi	2.50 ubuningi
	RO₂		%	0.4 ubuningi	0.40 ubuningi	0.40 ubuningi
Specific Surface Aea			cm³/g	3000ubuningi	3000ubuningi	350 imiz
Isethi Yokuqala			imiz	60 imiz	60 imiz	90 imiz
Iqeda Isethi			h	6 ubuningi	6 ubuningi	6 imiz
Ukugoba Amandla		1 usuku	Mpa	5.50 ubuningi	7.00 min	8.00 imiz
Ukugoba Amandla		3 usuku	Mpa	6.50 ubuningi	8.00 imiz	10.00 min
Amandla Acindezelayo		1 usuku	Mpa	40.00 ubuningi	50.00 min	72.00 min
Amandla Acindezelayo		3 usuku	Mpa	50.00 ubuningi	60.00 min	82.00 min
Ama-Refractories			℃	1350	1350	1450

I-Calcium Alumina Cement

Izinto			Iyunithi	CA-70	CA-80
Ukwakheka kwamakhemikhali	Al₂O₃		%	68.50-72.00	78.50-81.00
	I-CaO		%	28.0-31.50	17.00-20.00
	SiO₂		%	≤0.50	≤0.40
	Fe₂O₃		%	≤0.50	≤0.30
	K₂O+Na₂O		%	≤0.50
Specific Surface Aea			Cm²/g	≥5000	≥7000
Isethi Yokuqala			imiz	≥45	≥30
Iqeda Isethi			h	≤6	≤6
Ukugoba Amandla		24h	Mpa	≥7.0	≥5.50
Iyacindezela Amandla		24h	Mpa	≥45	≥40
Ama-Refractories			℃	≥1600	≥1790